Your Cart

WEICON Zinc Spray anti-corrosion agent 400ml [11000400-51]

WEICON Zinc Spray anti-corrosion agent 400ml [11000400-51]
WEICON Zinc Spray anti-corrosion agent 400ml [11000400-51]
WEICON Zinc Spray anti-corrosion agent 400ml [11000400-51]
WEICON Zinc Spray anti-corrosion agent 400ml [11000400-51]
WEICON Zinc Spray anti-corrosion agent 400ml [11000400-51]
WEICON Zinc Spray anti-corrosion agent 400ml [11000400-51]
WEICON Zinc Spray anti-corrosion agent 400ml [11000400-51]
WEICON Zinc Spray anti-corrosion agent 400ml [11000400-51]
WEICON Zinc Spray anti-corrosion agent 400ml [11000400-51]
WEICON Zinc Spray anti-corrosion agent 400ml [11000400-51]
WEICON Zinc Spray anti-corrosion agent 400ml [11000400-51]
WEICON Zinc Spray anti-corrosion agent 400ml [11000400-51]
WEICON Zinc Spray anti-corrosion agent 400ml [11000400-51]
WEICON Zinc Spray anti-corrosion agent 400ml [11000400-51]
WEICON Zinc Spray anti-corrosion agent 400ml [11000400-51]
WEICON Zinc Spray anti-corrosion agent 400ml [11000400-51]
WEICON Zinc Spray anti-corrosion agent 400ml [11000400-51]
WEICON Zinc Spray anti-corrosion agent 400ml [11000400-51]
WEICON Zinc Spray anti-corrosion agent 400ml [11000400-51]
  • Code: 10037443
  • In Stock: 8 pcs.
Updated: 22.07.2025 08:25
Details
Original YES
8.46€/pcs.

Description

WEICON Zinc Spray is a high-performance corrosion protection spray for long-term coating of metal surfaces. It forms a quick-drying, well-adhering protective layer made of ultra-pure zinc and aluminum particles (99.9%). Suitable for both indoor and outdoor use, including galvanized components. Offers excellent resistance to weather, salt spray, abrasion, and temperatures from -50°C to +500°C.

Typical applications:

  • Coating of outdoor-exposed metal parts

  • Protection of weld seams and drilled holes

  • Sealing exposed edges of galvanized components

  • Conductive base for spot welding

Technical details:

  • Color: RAL 9006 (dark hot-dip zinc)

  • Use: indoor and outdoor

  • Binder: alkyd styrene

  • Pigment content: approx. 99.9% Zn / 99.9% Al

  • Metal content in dry film: 70%

  • Application temperature: +5°C to +35°C (optimum +18°C to +35°C)

  • Dry to touch: 15 minutes

  • Fully cured: 12 hours

  • Temperature resistance: -50°C to +500°C

  • Abrasion resistant: yes

  • Salt spray test: >1050 h (DIN 53167 / DIN 50021)

  • Flexibility and adhesion: no microcracks, cross-cut GT 0

  • ISSA-Code: 53.402.06

  • IMPA-Code: 450811